$Kilns' Refractory Materials Heat Insulation Ceramic Fiber Blanket$ $Kilns' Refractory Materials Heat Insulation Ceramic Fiber Blanket$

Kilns' Refractory Materials Heat Insulation Ceramic Fiber Blanket

Category： Kilns' Refractory Materials
Classification temperature: 1260℃
Heat Linear Shrinkage:1000℃*24h≤4
Shot Content（φ≥0.212mm) ≤20%
Tensile Strength: ≥0.04 MPa
INQUIRY EMAIL

Kilns' Refractory Materials Heat Insulation Ceramic Fiber Blanket

1. Brief introduction

The ceramic fiber blanket is made from special aluminum silicate ceramic fiber using a double-sided needle process. The degree of fiber entanglement, delamination resistance, tensile strength and surface flatness are significantly improved after the double-sided necessity process. In addition, the fiber mat does not contain any organic binders to ensure that the ceramic fiber mat has good processability and stability at high and low temperatures.

2. Main technical parameters

Product Category	Normal Ceramic Fiber Blanket	Standard Ceramic Fiber Blanket	High Purity Ceramic Fiber Blanket	High Alumina Ceramic Fiber Blanket	Low Zirconium Ceramic Fiber Blanket	Zirconium Ceramic Fiber Blanket
Classification Temperature	1050	1260	1260	1350	1350	1430
Heat Linear Shrinkage	950℃*24h≤4	1000℃*24h≤4	1100℃*24h≤4	1200℃*24h≤4	1250℃*24h≤4	1350℃*24h≤4
Shot Content（φ≥0.212mm）%	≤20	≤20	≤15	≤15	≤15	≤15
Tensile Strength（mpa）(Thickness 25mm)	≥0.04	≥0.04	≥0.04	≥0.04	≥0.04	≥0.04
Thermal Conductivity（average 500℃）w/(m*K)	≤0.153	≤0.153	≤0.153	≤0.153	≤0.153	≤0.153
Density （kg/m3）	96/128(Others customized)
Size	Length（3600/4500/5000/7200）* Width（610/1200）* Thickness（6-60）

3. Typical application

Industrial kiln, heating device wall lining and back lining thermal insulation.
High temperature kiln, heating device, wall lining and gap filler.
Raw materials for high temperature gasket, module, folding block
High temperature equipment’s thermal insulation
High temperature pipeline’s thermal insulation
Electric component’s thermal insulation and fire prevention.